ASTM D885/D885M-10
Historical Standard: ASTM D885/D885M-10 Standard Test Methods for Tire Cords, Tire Cord Fabrics, and Industrial Filament Yarns Made from Manufactured Organic-Base Fibers
SUPERSEDED (see Active link, below)
ASTM D885 / D885M
1. Scope
1.1 These test methods cover the testing of industrial filament yarns made wholly of manufactured organic-base fibers, cords twisted from such yarns, fabrics woven from such cords, and products that are made specifically for use in the manufacture of pneumatic tires. They may be applied to similar yarns and cords used for reinforcing other rubber goods and for other industrial applications. The test methods apply to nylon, polyester, and rayon yarns and tire cords twisted from such yarns and to fabrics made from such cords. The yarn or cord may be wound on cones, tubes, bobbins, spools, or beams; may be woven into fabric; or may be in some other form. The methods include testing procedure only and include no specifications or tolerances.
1.2 No procedure is included for the determination of fatigue resistance of cord, but several commonly used procedures for the measurement of fatigue resistance of cords in rubber were published in the appendix of these test methods in the 1967 Annual Book of ASTM Standards , Part 24, and in earlier issues of Test Methods D885.
1.3 The sections on Growth of Conditioned Yarns and Cords, Properties of Yarns and Cords at Elevated Temperature, and Properties of Wet Yarns and Cords have been moved to Appendix X1-Appendix X3 as non-mandatory informational items because of their very limited use by the industry and because precision and bias statements are not included.
2. Referenced Documents (purchase separately) The documents listed below are referenced within the subject standard but are not provided as part of the standard.
ASTM Standards
D76 Specification for Tensile Testing Machines for Textiles
D123 Terminology Relating to Textiles
D276 Test Methods for Identification of Fibers in Textiles
D1423 Test Method for Twist in Yarns by Direct-Counting
D1776 Practice for Conditioning and Testing Textiles
D1777 Test Method for Thickness of Textile Materials
D1907 Test Method for Linear Density of Yarn (Yarn Number) by the Skein Method
D1909 Standard Table of Commercial Moisture Regains for Textile Fibers
D2257 Test Method for Extractable Matter in Textiles
D2258 Practice for Sampling Yarn for Testing
D2462 Test Method for Moisture in Wool by Distillation With Toluene
D2494 Test Method for Commercial Mass of a Shipment of Yarn or Manufactured Staple Fiber or Tow
D2654 Test Method for Moisture in Textiles
D3774 Test Method for Width of Textile Fabric
D3775 Test Method for Warp (End) and Filling (Pick) Count of Woven Fabrics
D3776 Test Methods for Mass Per Unit Area (Weight) of Fabric
D4393 Test Method for Strap Peel Adhesion of Reinforcing Cords or Fabrics to Rubber Compounds
D4776 Test Method for Adhesion of Tire Cords and Other Reinforcing Cords to Rubber Compounds by H-Test Procedure
D4848 Terminology Related to Force, Deformation and Related Properties of Textiles
D6477 Terminology Relating to Tire Cord, Bead Wire, Hose Reinforcing Wire, and Fabrics
Keywords
commercial mass; dip pickup; industrial yarn; linear density; manufactured fibers; moisture regain; shrinkage; tensile properties/tests; tire cord; tire fabric; twist; Breaking strength/tenacity--textile fabrics/fibers; Commercial mass; Density--linear; Diameter--textile fabrics/fibers; Dip pickup (DPU); Elongation--textiles; Man-made textile fibers; Polyester plastics; Rubber adhesion; Shrinkage--textile fabrics/fibers; Tensile properties/testing--textile materials/applications; Thickness--textile fabrics/fibers; Tire cords and tire cord fabrics; Twist--textiles; Wet testing; Work-to-break; Yarn number; Yarn properties--industrial yarns; Modulus; Moisture analysis--textile fabrics/fibers; Mass--commercial mass;
ICS Code
ICS Number Code 83.160.01 (Tyres in general)
DOI: 10.1520/D0885_D0885M-10
ASTM International is a member of CrossRef.