Significance and Use

The splitting tensile-strength test can be used only on brittle waste materials such as ceramics, glass, concrete, or other materials that also have tensile fracture strengths that are less than one third of the compression strengths.

1. Scope

1.1 This test method is used to measure the static splitting tensile strength of cylindrical specimens of brittle nuclear waste forms. It provides splitting tensile-strength data that can be used to compare the strength of waste forms when tests are done on one size of specimen.

1.2 The test method is applicable to glass, ceramic, and concrete waste forms that are sufficiently homogeneous (Note 1) but not to coated-particle, metal-matrix, bituminous, or plastic waste forms, or concretes with large-scale heterogeneities. Cementitious waste forms with heterogeneities >1 to 2 mm and 5 mm can be tested using this procedure provided the specimen size is increased from the reference size of 12.7 mm diameter by 6 mm length, to 51 mm diameter by 100 mm length, as recommended in Test Method C 496 and Practice C 192.

Note 1Generally, the specimen structural or microstructural heterogeneities must be less than about one-tenth the diameter of the specimen.

1.3 This test method can be used as a quality control check on brittle waste forms and may be useful for optimizing waste form processing. Meaningful comparison of waste forms, however, requires data obtained on specimens of one size.

1.4 The values stated in SI units are to be regarded as the standard.

1.5 This standard may involve hazardous materials, operations, and equipment. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. For specific hazard statements, see Section 7.

2. Referenced Documents (purchase separately) The documents listed below are referenced within the subject standard but are not provided as part of the standard.

ASTM Standards

C39/C39M Test Method for Compressive Strength of Cylindrical Concrete Specimens

C192/C192M Practice for Making and Curing Concrete Test Specimens in the Laboratory

C496/C496M Test Method for Splitting Tensile Strength of Cylindrical Concrete Specimens

C773 Test Method for Compressive (Crushing) Strength of Fired Whiteware Materials

D2938 Test Method for Unconfined Compressive Strength of Intact Rock Core Specimens

E4 Practices for Force Verification of Testing Machines

Society of Manufacturing Engineers

Keywords

nuclear scrap and waste materials; tension (tensile) properties/tests-tensile strength;

ICS Code

ICS Number Code 13.030.30 (Special wastes)